Strontium Dry Pressing Ferrite Magnetic compound are suitable for producing magnets by dry pressing. Strontium ferrite material features better magnetic property than barium ferrite material in the area of remanence induction intensity, coercivity and magnetic hysteresis loss.
Strontium compound have been added proper quantity of binders and lubricants and pass through 120 mesh sieve,so as binders to be uniformly distributed for better orientation. We could supply the compound in both spray dried or vibration granulated form.
| Type | Br | HCB | HCJ | (BH)max | Sintered density | ||||
| Grade | mT | Gs | KA/m | Oe | KA/m | Oe | KJ/m3 | MGOe | P(g/cm3) |
| YXC-C1T | 230 | 2300 | 150 | 1880 | 240 | 3010 | 9.50 | 1.19 | 4.6±0.2 |
| YXC-C2T | 230 | 2300 | 155 | 1950 | 278 | 3500 | 9.60 | 1.20 | 4.6±0.2 |
| YXC-C3T | 210 | 2100 | 150 | 1880 | 350 | 4400 | 9.00 | 1.13 | 4.6±0.2 |
| YXC-C1 | 370 | 3700 | 215 | 2700 | 231 | 2900 | 24.6 | 3.08 | 4.6±0.2 |
| YXC-C2 | 385 | 3850 | 219 | 2750 | 231 | 2900 | 26.0 | 3.27 | 4.6±0.2 |
| YXC-C3 | 395 | 3950 | 231 | 2900 | 235 | 2950 | 28.8 | 3.60 | 4.6±0.2 |